Main Features

6063-T6

T6 temper 6063 has an ultimate tensile strength of at least 28,000 psi (196 MPa) and yield strength of at least 23,000 psi (165 MPa). In thicknesses of 0.124-inch (3.1 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.

6061-T6

T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (300 MPa) and yield strength of at least 35,000 psi (241 MPa). More typical values are 45,000 psi (310 MPa) and 40,000 psi (275 MPa), respectively.[4] In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties. The typical value for thermal conductivity for 6061-T6 at 77 °F is around 152 W/m K. A material data sheet [5] defines the fatigue limit under cyclic load as 14,000 psi (100 MPa) for 500,000,000 completely reversed cycles using a standard RR Moore test machine and specimen. Note that aluminum does not exhibit a well defined "knee" on its S-n graph, so there is some debate as to how many cycles equates to "infinite life". Also note the actual value of fatigue limit for an application can be dramatically affected by the conventional de-rating factors of loading, gradient, and surface finish.